Here we report on a study dealing with a self-assembling ethylene oxide-propylene oxide-ethylene oxide triblock copolymer (Pluronic L64) and an anionic surfactant, sodium dodecyl sulfate (SDS), that in water at 25 degrees C form an interesting micellar region (L-phase). We have investigated the sequence of micelle structures in this L-phase across a wide interval of copolymer concentrations using phase diagram determination, steady shear, and NMR self-diffusion (pulsed gradient spin-echo, PGSE) experiments. In solutions which have been prepared at moderately low copolymer concentrations (ca. 20 wt.% L64) we report on a transition from discrete micelles to bicontinuous aggregates on the addition of SDS. This change was mainly inferred from self-diffusion coefficient patterns (i.e., the variation of copolymers and surfactant diffusivity vs. SDS content). At midrange and at higher polymer concentrations (i.e., in the interval from 50 to 80 wt.% L64) the L-phase occurred with a bicontinuous structure which was not modified by the progressive addition of SDS. Such a bicontinuous structure was identified by the comparison of self-diffusion coefficients of both cosolutes and the bulk viscosity (i.e., the behavior of zero-shear viscosity vs. SDS).

Solution microstructures of the micellar phase of Pluronic L64/SDS/water system

L. COPPOLA
;
NICOTERA, ISABELLA
2010-01-01

Abstract

Here we report on a study dealing with a self-assembling ethylene oxide-propylene oxide-ethylene oxide triblock copolymer (Pluronic L64) and an anionic surfactant, sodium dodecyl sulfate (SDS), that in water at 25 degrees C form an interesting micellar region (L-phase). We have investigated the sequence of micelle structures in this L-phase across a wide interval of copolymer concentrations using phase diagram determination, steady shear, and NMR self-diffusion (pulsed gradient spin-echo, PGSE) experiments. In solutions which have been prepared at moderately low copolymer concentrations (ca. 20 wt.% L64) we report on a transition from discrete micelles to bicontinuous aggregates on the addition of SDS. This change was mainly inferred from self-diffusion coefficient patterns (i.e., the variation of copolymers and surfactant diffusivity vs. SDS content). At midrange and at higher polymer concentrations (i.e., in the interval from 50 to 80 wt.% L64) the L-phase occurred with a bicontinuous structure which was not modified by the progressive addition of SDS. Such a bicontinuous structure was identified by the comparison of self-diffusion coefficients of both cosolutes and the bulk viscosity (i.e., the behavior of zero-shear viscosity vs. SDS).
2010
Micelle microstructures; Pluronics; Shear-rheology; diffusometry; NMR
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.11770/123242
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 13
  • ???jsp.display-item.citation.isi??? 13
social impact