Novel stimuli-responsive hydrophilic microspheres were prepared by free radical polymerization of hydroxyethyl methacrylate (HEMA) and methacrylic acid (MA), as hydrophilic monomers, and N-isopropylacrylamide (NIPAAm) and N,N′-ethylenebisacrylamide (EBA), as thermo-sensitive monomer and crosslinker, respectively. Hydrophilic comonomers were introduced in the macromolecular network to synthesize materials with tunable thermal behavior. In addition, by introducing in the polymerization feed both a hydrophilic and a pH-sensitive monomer, such as MA, dual stimuli-responsive (pH and temperature) hydrogels were synthesized. The incorporation of monomers in the network was confirmed by infrared spectroscopy, while the network density and the shape of hydrogels was found to strictly depend on the concentration of monomers in the polymerization feed. Thermal analyses showed negative thermo-responsive behavior with pronounced water affinity of microspheres at a temperature lower than lower critical solution temperature (LCST). In our experiment, the LCST values of the hydrogels were in the range 34.6–37.5°C, close to the body temperature, and the amount of hydrophilic moieties in the polymeric network allows to collect shrinking/swelling transition temperatures higher than the LCST of NIPAAm homopolymers. In order to test the preformed materials as drug carriers, diclofenac diethylammonium salt (DDA) was chosen and drug entrapment percent was determined. Drug release profiles, in media at different temperature and pH, depend on hydrogels crosslinking degree and drug–bead interactions. By using semi-empirical equations, the release mechanism was extensively studied and the diffusional contribute was evaluated.

Negative thermo-responsive microspheres based on hydrolyzed gelatin as drug delivery device

Curcio M;PUOCI Francesco;Spizzirri UG;IEMMA Francesca;Cirillo G;Parisi OI;PICCI Nevio
2010-01-01

Abstract

Novel stimuli-responsive hydrophilic microspheres were prepared by free radical polymerization of hydroxyethyl methacrylate (HEMA) and methacrylic acid (MA), as hydrophilic monomers, and N-isopropylacrylamide (NIPAAm) and N,N′-ethylenebisacrylamide (EBA), as thermo-sensitive monomer and crosslinker, respectively. Hydrophilic comonomers were introduced in the macromolecular network to synthesize materials with tunable thermal behavior. In addition, by introducing in the polymerization feed both a hydrophilic and a pH-sensitive monomer, such as MA, dual stimuli-responsive (pH and temperature) hydrogels were synthesized. The incorporation of monomers in the network was confirmed by infrared spectroscopy, while the network density and the shape of hydrogels was found to strictly depend on the concentration of monomers in the polymerization feed. Thermal analyses showed negative thermo-responsive behavior with pronounced water affinity of microspheres at a temperature lower than lower critical solution temperature (LCST). In our experiment, the LCST values of the hydrogels were in the range 34.6–37.5°C, close to the body temperature, and the amount of hydrophilic moieties in the polymeric network allows to collect shrinking/swelling transition temperatures higher than the LCST of NIPAAm homopolymers. In order to test the preformed materials as drug carriers, diclofenac diethylammonium salt (DDA) was chosen and drug entrapment percent was determined. Drug release profiles, in media at different temperature and pH, depend on hydrogels crosslinking degree and drug–bead interactions. By using semi-empirical equations, the release mechanism was extensively studied and the diffusional contribute was evaluated.
2010
hydrogel, hydrolyzed gelatin, microspheres, radical polymerization, thermo-responsive release
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.11770/128510
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 27
  • ???jsp.display-item.citation.isi??? 22
social impact