In recent years, Membrane Distillation (MD) has emerged either as a promising alternative or as a complement to Reverse Osmosis (RO) in seawater desalination. However, the performance of MD is significantly offset by temperature polarization, a phenomenon intrinsically related to water evaporation that causes the decrease of the solution temperature at the membrane surface and, ultimately, the loss of driving force. In this work, we show that temperature polarization can be withdrawn by exploiting thermal collective effects activated by the excitation of plasmonic modes in UV-irradiated Mixed Matrix Membranes composed of silver nanoparticles (Ag NPs) incorporated in polyvinylidene (PVDF) microporous films. For experimental tests carried out under vacuum (VMD) and with an absorbed radiant heating power of 2.3 · 104 W/m2, best results were obtained using PVDF membranes loaded with 25%Ag NPs. In this case, measured transmembrane fluxes to pure water and 0.5 M NaCl solution were 32.2 and 25.7 L/m2 h, respectively, i.e. about 11- and 9- fold higher than the corresponding values for unloaded membranes. Remarkably, energy analysis revealed that the heat generation of Ag NPs under plasmonic resonance was able to withdrawn temperature polarization, resulting in estimated temperature polarization factor (TPF) values of 106.5% for 0.5 M NaCl solution.

Overcoming the temperature polarization in membrane distillation by thermoplasmonic effects activated in Ag nanofillers in polymeric membranes

Politano, Antonio;Di Profio, Gianluca;Fontananova, Enrica;Cupolillo, Anna;Curcio, Efrem
2019-01-01

Abstract

In recent years, Membrane Distillation (MD) has emerged either as a promising alternative or as a complement to Reverse Osmosis (RO) in seawater desalination. However, the performance of MD is significantly offset by temperature polarization, a phenomenon intrinsically related to water evaporation that causes the decrease of the solution temperature at the membrane surface and, ultimately, the loss of driving force. In this work, we show that temperature polarization can be withdrawn by exploiting thermal collective effects activated by the excitation of plasmonic modes in UV-irradiated Mixed Matrix Membranes composed of silver nanoparticles (Ag NPs) incorporated in polyvinylidene (PVDF) microporous films. For experimental tests carried out under vacuum (VMD) and with an absorbed radiant heating power of 2.3 · 104 W/m2, best results were obtained using PVDF membranes loaded with 25%Ag NPs. In this case, measured transmembrane fluxes to pure water and 0.5 M NaCl solution were 32.2 and 25.7 L/m2 h, respectively, i.e. about 11- and 9- fold higher than the corresponding values for unloaded membranes. Remarkably, energy analysis revealed that the heat generation of Ag NPs under plasmonic resonance was able to withdrawn temperature polarization, resulting in estimated temperature polarization factor (TPF) values of 106.5% for 0.5 M NaCl solution.
2019
Membrane distillation; Thermoplasmonics; Photothermal effects; Surface plasmon resonance; Seawater desalination
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.11770/276950
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 105
  • ???jsp.display-item.citation.isi??? 98
social impact