Composite material prepared from polyethylene oxide (PEO) and polyvinylpyrrolidone (PVP) doped with Sodium (meta)periodate (NaIO4) salt was studied by complex impedance spectroscopy at room temperature. The polymers PEO and PVP were mixed in a weight ratio 70:30 %, and the concentration of the embedded NaIO4 compound was 7.5 wt.%. The effect from NaIO4 filler on the dielectric permittivity of the three-component mixed system was analyzed in the frequency range 0.1 Hz – 1 MHz. As compared with the two-component polymer host PEO/PVP, a distinctly enhanced electrical and dielectrical response and an increase of the value of dielectric constant of the polymeric (PEO/PVP):NaIO4 composite were present. This suggests the potential of this material for soft electronics and applications such as solid electrolytes.
Dielectric and electrical behaviours of polymeric (PEO/PVP):NaIO4 composite for solid electrolytes
SCARAMUZZA, Nicola
2017-01-01
Abstract
Composite material prepared from polyethylene oxide (PEO) and polyvinylpyrrolidone (PVP) doped with Sodium (meta)periodate (NaIO4) salt was studied by complex impedance spectroscopy at room temperature. The polymers PEO and PVP were mixed in a weight ratio 70:30 %, and the concentration of the embedded NaIO4 compound was 7.5 wt.%. The effect from NaIO4 filler on the dielectric permittivity of the three-component mixed system was analyzed in the frequency range 0.1 Hz – 1 MHz. As compared with the two-component polymer host PEO/PVP, a distinctly enhanced electrical and dielectrical response and an increase of the value of dielectric constant of the polymeric (PEO/PVP):NaIO4 composite were present. This suggests the potential of this material for soft electronics and applications such as solid electrolytes.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.