Industrial application of magnesium alloy AZ31 is dramatically increasing due to the very competitive mechanical strength vs. weight ratio. On the other hand, AZ31 is very difficult to be formed at room temperature. In this study incremental forming of the above material is taken into account, with particular reference to formability limits. The role of the main process parameters on material formability was investigated through a wide experimental campaign and a rigorous statistical analysis.
Warm incremental forming of magnesium alloy AZ31
AMBROGIO, Giuseppina;FILICE, Luigino;
2008-01-01
Abstract
Industrial application of magnesium alloy AZ31 is dramatically increasing due to the very competitive mechanical strength vs. weight ratio. On the other hand, AZ31 is very difficult to be formed at room temperature. In this study incremental forming of the above material is taken into account, with particular reference to formability limits. The role of the main process parameters on material formability was investigated through a wide experimental campaign and a rigorous statistical analysis.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.