Electro optic properties of switchable gratings made of polymer and nematic liquid crystal slices

We report the diffraction properties at wavelengths of 632.8 and 1550 nm for volume transmission gratings made of a sequence of continuously aligned nematic liquid-crystal layers separated by isotropic polymer slices. The gratings are generated by holographically curing a solution of liquid crystal diluted in an isotropic prepolymer by means of a laser beam at a wavelength of 352 nm with a total intensity of approximately 10 mW/cm2 . A diffraction efficiency of 98% was measured, and an electric field as low as 5 V/μm switches off the phase grating. Measured angular spectra are fitted by use of the modified coupled-mode theory including the effects of grating birefringence.

Vengono trattate le proprietà diffrattive a lunghezze d'onda di 632.8 e 1550 nm per reticoli di volume in trasmissione realizzati da una sequenza di piani di cristallo liquido uniformemente allineati separati da strati isotropi di polimero. I reticoli sono stati fabbricati tramite curaggio olografico, ad una lunghezza d'onda di 352 nm, di una soluzione di cristallo liquido diluito da un pre-polimero isotropo. E' stata misurata un'efficienza di diffrazione del 98% ed un campo elettrico di commutazione pari a 5 V/μm è sufficiente a commutare completamente il reticolo di fase. Gli spettri angolari misurati sono stati verificati teoricamente tramite un modello ai modi accoppiati che prevede gli effetti della birifrangenza del reticolo.