Novel magnetite-supported palladium catalysts, in the form of nanofiber materials, were prepared by using the electrospinning process. Two different synthetic techniques were used to add palladium to the nanofibers: (i) the wet impregnation of palladium on the Fe3O4 electrospun support forming the Pd/Fe3O4[wnf] catalyst or (ii) the direct co-electrospinning of a solution containing both metal precursor specimens leading to a Pd/Fe3O4[cnf] sample. The obtained Pd-based Fe3O4 nanofibers were tested in the transfer hydrogenolysis of benzyl phenyl ether (BPE), one of the simplest lignin-derived aromatic ethers, by using 2-propanol as H-donor/solvent, and their performances were compared with the analogous impregnated Pd/Fe3O4 catalyst and a commercial Pd/C. A morphological and structural characterization of the investigated catalysts was performed by means of SEM-EDX, TGA-DSC, XRD, TEM, H2-TPR, and N2 isotherm at 77 K analysis. Pd/Fe3O4[wnf] was found to be the best catalytic system allowing a complete BPE conversion after 360 min at 240◦C and a good reusability in up to six consecutive recycling tests.

Pd/Fe3O4 nanofibers for the catalytic conversion of lignin-derived benzyl phenyl ether under transfer hydrogenolysis conditions

Macario A.;Frontera P.
2020-01-01

Abstract

Novel magnetite-supported palladium catalysts, in the form of nanofiber materials, were prepared by using the electrospinning process. Two different synthetic techniques were used to add palladium to the nanofibers: (i) the wet impregnation of palladium on the Fe3O4 electrospun support forming the Pd/Fe3O4[wnf] catalyst or (ii) the direct co-electrospinning of a solution containing both metal precursor specimens leading to a Pd/Fe3O4[cnf] sample. The obtained Pd-based Fe3O4 nanofibers were tested in the transfer hydrogenolysis of benzyl phenyl ether (BPE), one of the simplest lignin-derived aromatic ethers, by using 2-propanol as H-donor/solvent, and their performances were compared with the analogous impregnated Pd/Fe3O4 catalyst and a commercial Pd/C. A morphological and structural characterization of the investigated catalysts was performed by means of SEM-EDX, TGA-DSC, XRD, TEM, H2-TPR, and N2 isotherm at 77 K analysis. Pd/Fe3O4[wnf] was found to be the best catalytic system allowing a complete BPE conversion after 360 min at 240◦C and a good reusability in up to six consecutive recycling tests.
2020
Aromatic ethers; Benzyl phenyl ether; Electrospinning; Heterogeneous catalysis; Iron oxide; Lignin; Palladium; Transfer hydrogenolysis
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.11770/303748
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 21
  • ???jsp.display-item.citation.isi??? ND
social impact