A comparative analysis of the low temperature resistance for a nanocarbon bitumen and other 30 neat and modified bitumens has been performed in the work. The stiffness at the temperatures of -24°С,-30°С and-36°С under technical system Superpave has been accepted as an indicator of low temperature resistance of the bitumens. The stiffness of the bitumens has been determined on a bending beam rheometer (standard ASTM D 6648-08). Before testing the bitumens have been subjected to the double artificial aging: Short-term aging - under standard AASHTO Т 240-13 and long-term aging - under standard ASTM D 6521-08. The nanocarbon bitumen has been prepared in the laboratory of the Kazakhstan Highway Research Institute (KazdorNII) with the use of a road bitumen of the grade BND 70/100 produced by the Pavlodar petrochemical plant (PNHZ) and a nanocarbon powder (2% by weight) manufactured from a coal rock of the deposit “Saryadyr” “Corporation “ON-Olzha” LLP, Akmola region, Kazakhstan). The nanocarbon powder (150-200 nm) has been manufactured by three-stage size reduction of the coal rock: I - a mechanical dispergator (up to 2-3 mm), II - an aerodynamic mill (up to 20 mcm), III - a reactor with a rotating electromagnetic field. The neat bitumens of the grades BND 50/70, BND 70/100, BND 100/130 have been produced by the plants of Kazakhstan and Russia; they satisfy the requirements of the standard ST RK 1373-2013. The modified bitumens have been prepared in the laboratory of KazdorNII with the use of the neat bitumens, 7 types of the polymers, crumb rubber and polyphosphoric acid and they satisfy the requirements of the standard ST RK 2534-2014. It has been determined that the nanocarbon bitumen is one of the most resistant at the low temperatures: -24°С,-30°С and-36°С.
Comparative analysis of low temperature resistance for nanocarbon and other bitumens
oliviero Rossi C.;
2020-01-01
Abstract
A comparative analysis of the low temperature resistance for a nanocarbon bitumen and other 30 neat and modified bitumens has been performed in the work. The stiffness at the temperatures of -24°С,-30°С and-36°С under technical system Superpave has been accepted as an indicator of low temperature resistance of the bitumens. The stiffness of the bitumens has been determined on a bending beam rheometer (standard ASTM D 6648-08). Before testing the bitumens have been subjected to the double artificial aging: Short-term aging - under standard AASHTO Т 240-13 and long-term aging - under standard ASTM D 6521-08. The nanocarbon bitumen has been prepared in the laboratory of the Kazakhstan Highway Research Institute (KazdorNII) with the use of a road bitumen of the grade BND 70/100 produced by the Pavlodar petrochemical plant (PNHZ) and a nanocarbon powder (2% by weight) manufactured from a coal rock of the deposit “Saryadyr” “Corporation “ON-Olzha” LLP, Akmola region, Kazakhstan). The nanocarbon powder (150-200 nm) has been manufactured by three-stage size reduction of the coal rock: I - a mechanical dispergator (up to 2-3 mm), II - an aerodynamic mill (up to 20 mcm), III - a reactor with a rotating electromagnetic field. The neat bitumens of the grades BND 50/70, BND 70/100, BND 100/130 have been produced by the plants of Kazakhstan and Russia; they satisfy the requirements of the standard ST RK 1373-2013. The modified bitumens have been prepared in the laboratory of KazdorNII with the use of the neat bitumens, 7 types of the polymers, crumb rubber and polyphosphoric acid and they satisfy the requirements of the standard ST RK 2534-2014. It has been determined that the nanocarbon bitumen is one of the most resistant at the low temperatures: -24°С,-30°С and-36°С.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.