In the present work a laboratory evaluation of the low-temperature rheological properties of neat andpolyphosphoric acid (PPA) modified bitumens by using a Dynamic Mechanical Analyzer (DMA) is presented.Fundamental rheological properties were evaluated in controlled kinematic conditions and theresults obtained were compared with traditional procedures such as the Fraass breaking point. Theresults show that the effect of polyphosphoric acid addition at low temperature is strongly dependenton bitumen composition (i.e. wax and asphaltene content), nevertheless it seems that PPA is able todecrease the glass transition temperature (Tg) and to increase the stiffness, improving the low temperatureperformance of the modified materials.

Low temperature rheology of polyphosphoric acid (PPA) added bitumen

Baldino N;GABRIELE, DOMENICO
;
OLIVIERO ROSSI, Cesare;Seta L;Lupi FR;Caputo P.
2012-01-01

Abstract

In the present work a laboratory evaluation of the low-temperature rheological properties of neat andpolyphosphoric acid (PPA) modified bitumens by using a Dynamic Mechanical Analyzer (DMA) is presented.Fundamental rheological properties were evaluated in controlled kinematic conditions and theresults obtained were compared with traditional procedures such as the Fraass breaking point. Theresults show that the effect of polyphosphoric acid addition at low temperature is strongly dependenton bitumen composition (i.e. wax and asphaltene content), nevertheless it seems that PPA is able todecrease the glass transition temperature (Tg) and to increase the stiffness, improving the low temperatureperformance of the modified materials.
2012
Dynamic Mechanical Analysis (DMA); bitumen; rheology
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.11770/142511
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 105
  • ???jsp.display-item.citation.isi??? 87
social impact